permanent magnetic materials introduction, classification, development history
These are the major permanent magnet material currently on the market, and someothers because of the production process or cost reasons, are not widely used even washed out such as Cu - Ni - Fe nickel iron (copper), Fe - Co - Mo iron, cobalt, molybdenum), Fe - Co - V (iron cobalt vanadium), MnBi manganese (bi)
according to the different production process can be divided into the following three:
Sintered neodymium magnets (Sintered NdFeB) - after airflow grinding powder and melting, Sintered NdFeB permanent magnets’ coercive force value is very high, and has extremely high magnetic energy, the maximum magnetic energy product (BHmax)is more than 10 times of Ferrite (Ferrite). Its mechanical properties are also very good, can cut into different shape and drilling. High-performance products of the highest working temperature can reach 220 degrees Celsius. Because of its material content is easy to cause corrosion, so according to different requirements it must be carried out surface coating treatment (such as galvanized zinc, nickel, environmental friendly zinc, environmental friendly nickle, nickel-copper-nickel). It is very hard and brittle, with high demagnetization resistance, high cost/performance ratio, is not suitable for high temperature working (> 220 ℃).
Bonded NdFeB (Bonded NdFeB) - Bonded NdFeB is NdFeB powder and resin, plastic or low melting point metal binder such as mixing, and then use methods such as compression, extrusion and injection molding compound made of NdFeB permanent magnets. Product forming at a time, without secondary processing, can be directly to make all kinds of complicated shape. Every direction of bonded ndfeb magnetic, can be processed into ndfeb compression mould and injection mould. Precision, magnetic is admirable, good corrosion resistance, high temperature stability is good.
Plastic injection NdFeB- made anisotropy has high precision, easy to shape complicated thin-walled rings or thin magnet
The main raw material of Sintered Ferrite (Sintered Ferrite) including BaFe12O19 and SrFe12O19, according to the orientation of the magnetic crystal divided into isotropic and different sex magnets. Because of its low price and moderate magnetic can become a magnet which has been widely applied at present. Ferrite magnets are made by ceramic technology, the quality of a material is solid, also is a brittle material, because of ferrite magnets have good temperature resistance and low prices, has become more widely applied permanent magnets.
Rubber magnetic (Rubber magnets) is one of the series of ferrite magnets, by binding with synthetic Rubber compound soft ferrite powder by extrusion molding, rolling molding, injection molding process and made of a soft, elastic and can distort the magnets. Can be processed into strips, roll, sheet and various kinds of complicated shape. Rubber magnet by magnetic powder (SrO6Fe2O3), polyethylene (CPE) and other additives (EBSO, DOP) etc, manufactured by extrusion, calendering. Rubber magnets can be the same or opposite sex, it is composed of ferrite magnetic powder, CPE, and some trace elements, can bend, twist, roll. It can be used without more mechanical processing, can also according to the required size trim shape, rubber magnetic, can also according to customer's requirement after PVC back glue, UV oil, etc. The magnetic energy product is between 0.60 to 1.50 MGOe. Rubber magnets application fields: refrigerators, message sign, will object fixed on the metal body of fasteners, such as used for advertising used in toys, teaching instrument, switch and sensor of the disk. Mainly used in micro motors, refrigerator, disinfection cabinet, kitchen cabinets, toys, stationery, advertising and other industries.
Aluminum nickel and cobalt (AlNiCo) is the earliest developed a kind of permanent magnetic material, is made from aluminum, nickel, cobalt, iron and other trace metal elements of an alloy. According to different production process can be divided into Sintered AlNiCo, Sintered AlNiCo) and casting aluminum nickel and cobalt (Cast AlNiCo). The product shape are round and square. Casting process can be processed into different size and shape; Compared with casting process, the sintering products is limited to small size, its production of blank size tolerance is better than blank casting products, magnetic is slightly less than the casting products, but it is better machinability. In the permanent magnetic material, casting aluminum nickel and cobalt permanent magnet has the lowest temperature coefficient is reversible, working temperature can be as high as 600 degrees Celsius above. Alnico permanent magnet products are widely used in all kinds of instruments and meters and other applications
Samarium cobalt (SmCo) according to the composition of different divided into SmCo5 and Sm2Co17, respectively was just generation and second generation rare earth permanent magnet materials. Due to its raw material is very scarce, expensive and make its development was restricted. Samarium cobalt (SmCo) as the second generation of rare earth permanent magnets, not only have higher magnetic energy product (14 to 28 mgoe) and reliable coercive force, and in the rare earth permanent magnet series shows good temperature characteristic. Compared with the ndfeb, samarium cobalt is more suitable for work in the environment of high temperature (>
With the development of the society, the application of the magnet is becoming more and more widely, from high-tech products to the most simple packaging, the most widely used or ndfeb strong magnetic and ferrite magnets.
From the development history of permanent magnetic material, the end of the 19th century the use of carbon steel, magnetic energy product (BH) Max (measure the quantity of the stored magnetic energy density permanent magnet) less than 1 mgoe high Mr (megabytes), and the foreign mass-produced Nd - Fe - B permanent magnet, magnetic energy product has reached more than 50 mgoe. This century, the material of remanent magnetism Br increase is very small, can improve due to product improvement of coercive force Hc. And coercive force increase, mainly thanks to the understanding of its nature and high magnetocrystalline anisotropy compounds are found, and the progress of the preparation technology. At the beginning of the 20th century, people mainly use carbon steel, tungsten, cobalt chromium steel and steel for permanent magnetic material. Developed in the late 1930 s, AlNiCo permanent magnet materials, makes the large-scale application of permanent magnet material possible. 50 s, the emergence of barium ferrite, reduces the cost of permanent magnets, and to broaden the application scope of permanent magnet materials to high frequency field. The emergence of cobalt to 60 s, rare earth permanent magnet, is for the application of permanent magnet has opened up a new era. In 1967, the United States at the university of Dayton Strnat etc., made by powder method successfully SmCo5 permanent magnets, marks the arrival of the era of rare earth permanent magnet. So far, diluted 10 permanent magnet has experienced the first generation of SmCo5, the second generation Sm2Co17 precipitation hardening type, development to the third generation of Nd - Fe - B permanent magnet materials. In addition, in history it is also used as a permanent magnetic material like I - Ni - Fe Cu, Fe, Co - Mo, Fe - Co - V, MnBi, A1MnC alloy, etc. These alloys due to performance is not high, the cost is not low, in most cases has been rarely used. And AlNiCo, FeCrCo and PtCo alloy is applied in some special occasions. At present, Ba, Sr ferrite still is one of the biggest amount of permanent magnetic material, but its many applications is gradually replaced by the Nd - Fe - B type material. And now the output value of the rare earth permanent magnet materials have greatly more than ferrite permanent magnet, rare earth permanent magnet material production has developed into a big industry.
"Since 2006, we found Mr.Guo and get products from him. We used magnets under the earth for the gas and water pipe industries. We have met no problem. We have been working in very happy ways. We have many cooperation. Every year, we spent time together and sometimes, we invited him to Korea. He is our younger brother. Strongly recommended!!"
--------Mr. Tae Lee Korea
"I had email to Mr. Guo for rare earth magnet requirements. They replied my e-mail promptly, and were very professional. Mr. Guo’s team still continues to deliver rare earth magnets to our agreed specifications with a very high quality standard since 2012. His team is very professional and thorough with its work. Based on my experience, I would highly recommend them."